Procedure modified by J. Whitsett, S. M. Condren, and G. Lisensky from
A. K. Bentley, M. Farhoud, A. B. Ellis, G. C. Lisensky, Anne-Marie Nickel, and W. C. Crone,
"Template Synthesis and Magnetic Manipulation of Nickel Nanowires,"
Journal of Chemical Education, 82,
765-768 (2005). Thanks to Anupam Ghosh for suggesting the ethanol storage. This version of the experiment uses a syringe holder, clamps, and an o-ring to hold the filter.
It uses more equipment than another version that uses electrical tape but the manipulation is easier.
A simple way to make nanowires is
to use a mold or template. In this experiment nickel nanowires are grown inside
the pores of an alumina filter and then the filter is removed by etching to
yield magnetic nanowires. Nanoporous membranes were designed for health care applications
including virus filtration, sample preparation, and liposome manufacture (anodisc filters).
These alumina membranes are manufactured by applying a large electrical potential
to a piece of aluminum metal submerged in an acid. Aluminum is oxidized to
alumina (Al2O3) and pores are created. The size of the
pores depends on the applied potential.
Avoid contact with or inhalation of nickel and nickel solutions.
Obtain a 0.02 micrometer Anodisc filter. These ceramic discs are
quite brittle and are supported by a polymer ring. Always use tweezers
to hold the membranes by the support ring; the alumina will crack if handled
directly. Remove the disc from the packaging, remembering which side was
up in the box. Discard the blue paper separator. Fully coat the upper side (the polymer ring looks wider)
with a conducting metal (see options in next steps).
One option is to use a cotton applicator and liquid GaIn alloy to
paint the surface. The coated side will look shiny (and the opposite side
will remain lighter.) While it is important to fully coat the surface
to prevent leaks, it is only necessary to dip the applicator in the GaIn
once. The GaIn can be spread quite thin. Check for gaps in the GaIn coating
by looking at the non-coated face of the membrane. Any areas without GaIn
will appear light blue in color while areas with GaIn will appear white
Another option is to sputter Ag metal onto the surface. Conditions
used were 50 millitorr argon, 45 milliamps current, for three 150 second
depositions. The coated side will look shiny (and the opposite side will
Place the copper electrode on the stand.
Place the disc, metal coated side down, on the copper electrode.
Place the o-ring on the disc.
Stand the cut-off syringe barrel on the o-ring.
Firmly hold the barrel in place while securing opposite sides of the
barrel with binder clamps. Look down the barrel of the syringe to make sure it is centered over the o-ring.
Record the dry weight of the nickel electrode before electrolysis.
What is the measured voltage of your 1.5 V battery?
Insert the battery into the battery holder, paying attention to polarity. The positive end should be connected to the nickel electrode.
Add nickel plating solution to the barrel up to the first markings. Check for leaks.
Connect the negative lead of the battery to a multimeter set to read current and then use a jumper cable to connect the multimeter to the copper stage.
Insert the nickel electrode into the nickel solution, start timing, and record the current passing through the circuit.
If no current flows, examine the apparatus to fix any bad electrical connections. Electrolyze for 20-45 minutes. What is the average current reading?
Longer times give longer wires unless the pore length is exceeded. How many minutes did you use?
Disconnect the battery from the copper electrode. Remove the nickel electrode from solution.
The nickel solution can be reused for this experiment. Why does the concentration of nickel in solution not change during the electrolysis?
Rinse the disc with water. Wait for the nickel electrode to dry and measure its weight.
Firmly hold the barrel in place and remove the binder clips. Transfer the disc from the copper electrode and
gently tape the disc shiny side up to a glass slide for removal of the metal coating.
In a fume hood, use concentrated nitric acid and a cotton applicator to remove the shiny GaIn or the Ag coating.
Soak the cotton applicator in water before disposal.
Rinse with water to remove the nitric acid. Even medium concentrations of nitric acid may slowly dissolve nickel.
Obtain the powder x-ray diffraction spectrum (2θ = 40-100°, step width 0.05, count 1.0s) of the nickel nanowires in the filter.
Place the wet filter on a glass microscope slide as a holder. Which side should be up? How similar is the spectrum to that of nickel metal?
Place the disc in 5 mL of 6 M NaOH for at least 10 minutes (plastic beaker preferred.) The ceramic
material will dissolve. Discard the polymer support ring.
Place the beaker on a strong magnet. The nickel nanorods will be attracted towards the magnet. Remove the NaOH solution. Add water to rinse, place
the beaker on a strong magnet, and remove the rinse solution. Repeat many times. (A common error in this experiment is insufficient rinsing.)
Transfer the final suspension to a vial for storage. Keep the wires in solution.
Obtain the powder x-ray diffraction spectrum (2θ = 40-100°) of the free nickel nanowires. To prepare the sample, wrap a piece of transparent tape very tightly around a microscope slide with the sticky side out. Use an XRD holder to position the tape at the correct distance from the end of the slide.
Puddle a fairly dense water suspension of the nanowires onto the tape and let dry enough that the wires stay put when tilted. If you do not have much sample, a strip oriented as shown in the figure is your best chance of getting data.
Use an SEM to measure the length of the nanowires. Does the length correlate with deposition time?
(Rinsing with ethanol and storing the nanowires in ethanol gives a suspension that leaves less residue and evaporates more quickly for preparation of samples.
To prepare the sample, first examine a nanowire solution under a visible microscope to check concentration. You want to be able to see individual nanowires rather than a mass of nanowires. Dilute the solution if necessary. Transfer the solution from the microscope to a small piece of silicon wafer and let the solution evaporate.)
Based on your reported electrolysis time and the average current, how many grams of nickel did you make? How does this vaue compare with the change in weight of the electrode?
How long are your nickel nanowires? You should measure this many times on more than one SEM image, take an average, and report all measured data. (ImageJ is useful for measuring lengths. Use the straight line tool to drag the length of the scale bar and menu Analyze/Set Scale to tell the program the actual length of the scale bar. You can then use the straight line tool to measure lengths in real units.) If the diameter of the wire is 200 nm and the density of nickel is 8.9g/cm3, how many wires did you make?
Is your product magnetic? How do you know? Report all observations relevant to your answer.
How could this apparatus be used to make nanowire barcodes? Provide a reference for your answer.
Does the XRD data show any evidence for a preferred crystal orientation of the nanowires in the filter? Which side of the filter did you examine with the x-rays? What is the ratio of the XRD (220) to (111) peak heights for nickel nanowires in the template, for free nickel nanowires, and for normal nickel metal?
GE Whatman Anodisc alumina filters 25mm with polypropylene support rings and
0.02 micrometer pores: Fisher Scientific (#09-926-34) or VWR International (#28138-067)
GaIn Eutectic: Aldrich (49542-5)
Ni wire: VWR International (#AA41361-G6) or Alfa Aesar 1 mm diameter x 10 m long. CAUTION: Avoid physical contact (especially inhalation) with nickel and
nickel solutions as nickel is an irritant and carcinogen.
"Watts" Nickel plating solution: 300g/L NiSO4.6H2O, 45g/L H3BO3
and 45g/L NiCl2.6H2O. (Oliver P. Watts was an electrochemist at the University of Wisconsin who studied nickel plating 100 years ago.)
Nitric acid (conc), 6 M NaOH
Tweezers, cotton swabs, water wash bottle, beaker
0.032 inch thick satin finish copper sheet, 12" x 12",
1-1/8" OD x 7/8" ID x 1/8" W o-ring (same diameter as the 1" syringe), Ace Hardware or
Make a hole in the end of the plunger for the positive lead of the battery holder.
Wires with alligator clips: Mouser (#13AC012)
To prepare the battery holders, cut in half a wire with
aligator clips on each end, strip off the insulation for a short distance, use a soldering iron to melt some solder onto each wire and onto the ends
of the battery holder, and then use a soldering iron to connect the wires
to the battery holder.
Nickel nanowires viewed through an optical microscope (20x) while
a magnet is moved back and forth from the front to the side of the microscope.
The nanowires rotate to align with the magnetic field. The scale bar represents
Nickel nanowires viewed through an optical microscope (20x) while
a magnet is spun at one side. The nanowires rotate to align with the magnetic
field. The scale bar represents 100 micrometers.
Nickel nanowires suspended in water controlled by a magnetic field.